0.7 Density Sodium Lauryl Sulfate 200℃ Softening Point Powder SLS
Product Introduction Of Powder SLS:
Ultra-narrow powder particle size distribution, improve the
flatness of the scraper, high accumulation density, ensure the
actual density of the workpiece.
According to the performance of laser sintering, this product is
modified first and then graded to ensure the utilization rate of
the return powder.
The softening point is close to the melting point, and the range of
preheating temperature for the powder in the molding equipment is
wide.
Good crystallinity, stable size and small thermal deformation.
Multi-size powder particle size distribution, height from 0.08 to
0.2mm.
Technical Data Of Powder SLS:
| Material performance items | Value | Units | Test standard |
| Actual density of material | 1.37 | g/cc | |
| Molding shrinkage | 0.1~0.3 | % | |
| Loose density | 0.71 | g/cc | |
| Particle size Distribution | D90 | 52 | um | |
| D50 | 38 | um | |
| D10 | 25 | um | |
| The density of fabrication | 1.24 | g/cc | |
| Melting point | 230 | ℃ | |
| Softening Point | 200 | ℃ | Ordinary pressure |
| Tensile strength | 130 | Mpa | ASTM D638 |
| Elongation at break | 36 | % |
| Notch impact strength | 6 | KJ/m³ | ISO 179 |
| Material preheating temperature | 160~200 | ℃ | |
| Molecular weight of material | 55000~ | 80000 | | |
Used for industrial production of high mechanical parts, hand mold,
wax mold before casting.
| Material performance items | Value | units | Test standard |
| Actual density of material | 1.03 | g/cc | |
| Molding shrinkage | 0.4~1.0 | % | |
| Loose density | 0.51 | g/cc | |
| Particle size distribution | D90 | 72 | um | |
| D50 | 51 | um | |
| D10 | 27 | um | |
| The density of fabrication | 0.98 | g/cc | |
| Melting point | 172 | ℃ | |
| Softening point | 107 | ℃ | Ordinary pressure |
| Tensile strength | 49.3 | Mpa | GB/T 1040-2006 |
| Elongation at break | 40 | % |
| Notch impact strength | 3.6 | KJ/m³ | GB/T 1043-2006 |
| Charpy Non-Notch Impact | 19 | KJ/ m³ |
| Material preheating temperature | 160 | ℃ | |
Hand mold, ornamental parts, high surface requirements
| Material performance items | Value | Units | Test standard |
| Actual density of material | 0.95 | g/cc | |
| molding shrinkage | 0.4~0.8 | % | |
| Bulk Density | 0.47 | g/cc | |
| particle size distribution | D90 | 65 | um | |
| D50 | 55 | um | |
| D10 | 23 | um | |
| The density of fabrication | 0.90 | g/cc | |
| melting point | 178 | ℃ | |
| softening point | 112 | ℃ | Ordinary pressure |
| tensile strength | 29.3 | Mpa | GB/T 1040-2006 |
| elongation at break | 15 | % |
| notch impact strength | 3.6 | KJ/m³ | GB/T 1043-2006 |
| Charpy Non-Notch Impact | 19 | KJ/ m³ |
| Material preheating temperature | 160 | ℃ | |
3D sand casting
Application Of Powder SLS:
Packaging&Shipping Of Powder SLS:
1)25kgs/bag, with composite kraft paper bag
2)palletizing, suitable for sea and air transportation
3)shrink film
4)ton bag
Our Services:
Our company makes both plastic powder and plastic powder making
machine
--- cryogenic grinder,mixing machine,sifting machine,feeding
machine,air classifier...etc
We have both chemical and mechanical engineers to provide you super
service.
Just tell us your usage or application!
--------- we CAN help you!
Production Machines Of Powder SLS:
If you want to make powder by yourself, we can also help you!
We make cryogenic grinder,air classifier,sifting machine,mixing
machines,feeding machines....etc,too.